Graphite/Carbon has the good property of good resistant-corrosion,high thermal conductivity and lower friction,good self-lubrication,the smaller expansion.They can be made into the seal faces,bearings and so on.It is ideal to choose it as the frictional mating rings.
| 碳石墨物理性能参数 Graphite/Carbon physical property | ||||||||
| 类别 Category | 型号Model | 体积密度 Density (g/cm3) | 弯曲强度 Flexural Strength (MPa) | 压缩强度Compressive Strength（MPa） | 肖氏硬度Shaw Hardness(HS) | 显气孔率Porosity Rate（%） | 使用温度Temperature（℃） | |
| 碳石墨 Carbon-graphite | 热压石墨Hotpressed Carbon | M1 | ＞1.65 | 65 | 150 | ＞70 | ＜0.2 | 180 |
| 模压烧结石墨 Sintered Carbon | MJ | ＞1.75 | 60 | 160 | ＞85 | ＜2.5 | 200 | |
| 浸环氧树脂 Impregnated Epoxy Resin(H) | M106H | 1.75 | 65 | 200 | 85 | ＜1.0 | 250 | |
| M120H | 1.70 | 60 | 180 | 80 | ＜1.0 | 250 | ||
| 浸呋喃树脂 Impregnated Furan Resin(K) | M106K | 1.75 | 67 | 200 | 90 | ＜1.0 | 250 | |
| M120K | 1.70 | 62 | 180 | 85 | ＜1.0 | 250 | ||
| 浸酚醛树脂 Impregnated Phenol Aldehyde Resin(F) | M106F | 1.75 | 60 | 200 | 85 | ＜1.0 | 250 | |
| M120F | 1.70 | 55 | 180 | 80 | ＜1.0 | 250 | ||
| 浸锑石墨Antimony Carbon(D) | M106D | 2.30 | 65 | 220 | 90 | ＜1.5 | 400 | |
| M120D | 2.30 | 60 | 220 | 90 | ＜1.5 | 400 | ||
| M254D | 2.30 | 55 | 210 | 65 | ＜1.5 | 400 | ||